The effect of organic additives, polyethylene glycol (PEG), on the trivalent chromium electroplating was analysed in the view point of current efficiency, solution stability and metallurgical structure. It was measured that PEG-containing trivalent chromium solution had about 10% higher current efficiency than pure solution and controlled the micro-crack density of electrodeposits. PEG exhibited profound effect on the solution stability by reducing the consumption rate of formic acid which acts as a complexant to lower the activation energy required for electrochemical reduction of trivalent chromium ions. It was also revealed that the formation of chromium carbide layer was facilitated in the presence of polyethylene glycol, which meant easier electrochemical codeposition of chromium and carbon, not single chromium deposition. Trivalent chromium layer formed from PEG-containing solution was amorphous with local nano-crystalline particles, which were prominently developed on the entire surface after non-oxidative heat treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Korean institute of surface engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.