Polycrystalline Silicon Films Formed by Solid-Phase Crystallization of Amorphous Silicon: the Substrate Effects on Crystallization Kinetics and Mechanism

Abstract

AbstractThe substrate effects on the solid-phase crystallization of amorphous silicon (a-Si) have been extensively investigated. The a-Si films were prepared on two kinds of substrates, a thermally oxidized Si wafer (SiO2/Si) and a quartz, by low-pressure chemical vapor deposition (LPCVD) using Si2H6 gas at 470 °C and annealed at 600 °C in an N2 ambient for crystallization. The analysis using XRD and Raman scattering shows that crystalline nuclei are faster formed on the SiO2/Si than on the quartz, and the time needed for the complete crystallization of a-Si films on the SiO2/Si is greatly reduced to 8 h from ˜15 h on the quartz. In this study, it was first observed that crystallization in the a-Si deposited on the SiO2/Si starts from the interface between the a-Si film and the thermal oxide of the substrate, called interface-induced crystallization, while random nucleation process dominates on the quartz. The very smooth surface of the SiO2/Si substrate is responsible for the observed interface-induced crystallization of a-Si films.