Abstract
AbstractPolyphenylsilsesquioxane (PPSQ) of ladder structure synthesized in laboratory was incorporated into polycarbonate (PC) by means of a twin‐screw extruder. Scanning electron microscopy (SEM) observations showed that spherical PPSQ particles of size 0.5−1.5 μm dispersed homogeneously in PC. The incorporation of PPSQ into PC improved the elongation at break and flexural strength. Thermal gravimetric analysis and Fourier transform infrared spectroscopy revealed that PPSQ made the initial thermal decomposition of PC happen fast. The early cleavages of CC and CO bonds in the PC chains induced crosslinking reaction in the condensed phase char. According to the cone calorimetry (CONE) tests, loading of 8 wt % PPSQ reduced the peak heat release rate of PC composites from 570 to 153 kW/m2. The chars obtained after CONE testing of PC/PPSQ composites showed continuous, smooth, flaky, and cascading char and SiO2 ceramic layer on the top. These indicated the good flame retardancy of PC/PPSQ, that is the attainment of a UL‐94 rating of V‐0 (1.6 mm), and limiting oxygen index of 42.0% when PPSQ was in 8 wt % in PC. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call