Poly (vinyl alcohol)/graphene oxide nanocomposite films and hydrogels prepared by gamma ray

Abstract

ABSTRACTPoly (vinyl alcohol)/graphene oxide (PVA/GO) gamma irradiated nanocomposite films and hydrogels were prepared. In composite films, GO was initially irradiated by gamma ray in order to improve interactions between GO and PVA. The film containing 1 wt-% GO was very strong where tensile modulus and tensile yield strength were 45 and 115% higher than those of pure PVA. In the second set of experiments PVA/GO hydrogels were made by irradiating PVA/GO suspensions by gamma ray at various doses. It was an interesting finding that GO increased the gel portion of hydrogels through contribution of H-bonds between PVA and GO. The hydrogels prepared at 20 kGy had remarkable water swelling ratio that reached as high as 20 at water temperature of 80°C. The hydrogel metal ion adsorption capability was tested on Cu2+ ions. It was shown that the GO contributed significantly to the adsorption capacity of PVA hydrogels.