Abstract
Cyano-functional polyether copolymers based on THF were prepared via cationic ring-opening copolymerization of THF with cyano ethylene oxide (CEO). The CEO content of poly(tetrahydrofuran) (polyTHF) based copolymers varied from 3.3 to 29.3%, and molecular weights ranged from 5100 to 31900 g·mol–1 with Mw/Mn in the range of 1.31 to 1.74 (SEC in THF, PS standards). The polymerization was conducted with methyl trifluoromethanesulfonate (MeOTf) as an initiator. Kinetic studies concerning incorporation of both monomers were performed via NMR spectroscopy. The cyano groups at the poly(THF-co-CEO) copolymers enable direct access to amino (polyTHF–NH2) and carboxyl groups (polyTHF–COOH) in facile one-step procedures, respectively. The modified copolymers were characterized via NMR, MALDI–ToF mass, and FT-IR spectroscopy. Thermal properties of the materials were studied via differential scanning calorimetry (DSC), demonstrating a gradual decrease of the melting points with increasing amount of CEO in the copolymer...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.