Abstract
High molecular weight poly(aryl ether ketone ketone)s comprising diphenyl-biphthalazin-dione moieties (P-MDs) were prepared through the solution condensation. The structure of polymers was characterized via nuclear magnetic resonance spectra and infrared absorption spectrum. The effects of mixed diphenyl-biphthalazin-dione (mDBD) monomer on performance of polymers were investigated. The mDBD units containing side phenyl groups endow polymer with solubility and controllable contact angle. The resultant polymers perform a fine thermo-stability in both nitrogen and air, presenting an excellent thermal resistance with glass transition temperature in the range of 253–333 °C. Simultaneously, the polymers exhibit a favorable solubility in 1,1,2,2-tetrachloroethane and N-methylpyrrolidone, showing fine film-formation performance. Polymers possess excellent mechanic performance with the tensile strength up to 84 MPa, the Young’s modulus above 1.5 GPa and the retention of storage modulus at 250 °C as high as 70%. Additionally, the contact angle of water-drops with polymer films is within the range of 73.5°–89.1°.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.