Abstract
The authors report the observation of strong polarization anisotropy in the photoluminescence (PL) and the absorption spectra of [112¯0] oriented A-plane wurtzite InN films grown on R-plane (11¯02) sapphire substrates using molecular beam epitaxy. For A-plane films the c axis lies in the film plane. The PL signal collected along [112¯0] with electric vector E⊥c is more than three times larger than for E‖c. Both PL signals peak around 0.67eV at 10K. The absorption edge for E‖c is shifted to higher energy by 20meV relative to E⊥c. Optical polarization anisotropy in wurtzite nitrides originates from their valence band structure which can be significantly modified by strain in the film. The authors explain the observed polarization anisotropy by comparison with electronic band structure calculations that take into account anisotropic in-plane strain in the films. The results suggest that wurtzite InN has a narrow band gap close to 0.7eV at 10K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.