Abstract
H2S and HCl are common impurities in raw syngas produced during gasification of biomass and municipal solid waste. The purpose of this study was to investigate the poisoning effect of H2S and HCl on synthesized and commercial catalysts during steam reforming of naphthalene. Four synthesized catalysts with different loadings of Ni and Fe on alumina support and two commercial catalysts were selected and evaluated in a fixed bed reactor at 790, 850 and 900 °C. The obtained results revealed that reforming and water-gas shift (WGS) activities of catalysts did not benefit from the Fe addition. The activities were influenced differently by H2S and HCl indicating that the reactions were catalyzed by different active sites on the nickel surface. In the presence of H2S and HCl, the poisoning of naphthalene reforming activity was caused by H2S and was not affected by HCl when both compounds were present in the gas. H2S chemisorbs on nickel surface forming NiS and decreasing the accessibility of active sites to hydrocarbons. The poisoning effect was only partially reversible. On the contrary, the poisoning of WGS activity could be caused by both H2S and HCl, and the activity could be completely restored when H2S and HCl were removed from the gas. Unlike naphthalene reforming activity, which was comparable for catalysts with similar Ni loadings, WGS activity depended on the catalyst structure and was less susceptible to poisoning by H2S and HCl in case of the catalyst with strong NiO-support interactions.
Highlights
Syngas obtained during biomass/municipal solid waste (MSW) gasification is mainly a mixture of carbon monoxide, carbon dioxide, hydrogen, methane and nitrogen, which can be utilized for electric power generation or liquid fuel synthesis [1]
The specific surface areas and total pore volumes of the synthesized catalysts decreased with increasing Ni + Fe contents, which can be attributed to the impregnation of the porous alumina with loaded metal species
X-ray diffraction (XRD) patterns of the synthesized catalysts in Fig. 2 consist of broad peaks with no distinct XRD peaks and show no sharp XRD peaks indicating that alumina, nickel and iron oxides have non-crystalline and/or nanosized structures, so that alumina provides surface area for better dispersion of catalyst
Summary
Syngas obtained during biomass/municipal solid waste (MSW) gasification is mainly a mixture of carbon monoxide, carbon dioxide, hydrogen, methane and nitrogen, which can be utilized for electric power generation or liquid fuel synthesis [1]. The biomass- and MSWderived syngas, contains significant concentrations of impurities such as tar, HCl, alkali chlorides, particulate matter, ammonia, HCN and sulfur compounds. Tar, consisting of a mixture of aromatic hydrocarbons, causes equipment failure by its condensation and corrosion upon cooling of syngas [2,3,4]. The techniques that can efficiently remove tar compounds to the acceptable levels are still under development. One of the prospective techniques is catalytic steam reforming which converts tar into H2 and CO [5,6,7]. The utilization of Ni-based catalysts enhances syngas production due to steam reforming of hydrocarbons and other catalyzed reactions, including dry reforming, WGS and Bodouard reactions [8,9,10,11,12]. Ni-based catalysts facilitate simultaneous decomposition of NH3 and HCN into N2 and H2
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.