Abstract
Even though Mg alloys containing Mn and rare earth elements lead to higher ductility and lower yield asymmetry due to the weak texture after extrusion, plastic instability, commonly known as the Portevin–Le Chatelier (PLC) effect, causes unexpected fragility in the service environment. In the present study, the PLC phenomenon and texture development during the deformation of Mg-Mn and Mg-Mn-Nd extruded alloys were investigated under various temperatures and strain rates. The addition of Nd causes not only texture weakening but also severe PLC phenomenon. The PLC phenomenon was significantly affected by the temperatures and the strain rates, which causes a difference in mechanical properties and development of texture. In the conditions of high temperature and low strain rate, the strength increased while the elongation decreased significantly, and obvious PLC phenomenon with severe serration and negative strain rate sensitivity. The initial texture was maintained even after deformation only under severe PLC conditions, and this is due to the restriction of basal slip and suppression of lattice rotation in PLC conditions. The series of results indicate that the PLC phenomenon causes a reduction of formability even at high temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.