Plastic anisotropy of ultra-thin rolled phosphor bronze foils and its thickness strain evolution in micro-deep drawing

Abstract

Metal foils are highly advantageous for producing microcomponents with high-aspect-ratio three-dimensional shapes by miniaturizing the process dimensions in sheet-metal-forming technologies. To characterize existing rolled metal foils at manufacturing sites and to clarify the impact of its strong anisotropic properties on micro-sheet formability, tensile tests and micro-deep drawing tests were performed on phosphor bronze foils with thicknesses of 20–300μm. Focusing on the Lankford value (r-value) as a useful parameter for conventional sheet-metal-formability, the relation between the r-value of ultra-thin rolled foil and its applicability in micro-deep drawing is investigated. Ultra-thin rolled foil is characterized with a higher r-value due to the strong texture of {110} and {111} textures. Although the in-plane tendency of the r-value showed a strong correlation with the thickness distribution of micro-drawn cups, the obtained higher r-value for thinner foils does not correspond to the lower formability of thinner metal foils. As relevant parameter for indicating the forming limit for thin-rolled metal foils, the nonuniformity in thickness due to surface roughening is introduced. The importance of a geometrical anisotropy, such as orientation of surface topography and defects, for the unstable deformation of ultra-thin rolled metal foils is experimentally demonstrated.