Abstract
In this work, oxide-free AlN coating was fabricated using single-step, large throughput nitrogen-shrouded plasma spraying. Initially, Al/AlN composite feedstock powder was prepared by a ball-milling at a 70:30 wt% ratio to deposit the AlN coating. Microstructural evaluation revealed the formation of dominant c-AlN phase along with minor h-AlN without presence of any oxides or impurities in the coating. Hardness and elastic modulus (E) were observed to be ∼7.2 GPa and ∼280 GPa respectively. Furthermore, an investigation of tribological performance showed the wear rate ∼0.18 × 10−3 mm3/Nm and coefficient of friction (COF) 0.45 ± 0.02. In addition, the corrosion resistance behaviour of AlN coating in 3.5 wt% NaCl shows as low as 2.95 × 10−9 mm/s indicates the extended life of the coated components. Therefore, the fabricated plasma-sprayed AlN coating can be recommended for high-performing wear and anti-corrosive competitor for industrial applications.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call