Abstract
The influence of plasma nitriding on mechanical, corrosion and tribological properties of Ti6Al4V has been investigated using X-ray diffraction, microhardness tester, scanning electron microscopy, pin-on-disc tribotester, electrochemical polarization and impedance spectroscopy. Plasma nitriding treatment of Ti6Al4V has been performed in 25%Ar–75%N 2 gas mixture, for treatment times of 1–4 h at the temperatures of 650–750 °C. The corrosion tests were carried out in Ringer solution at 37 °C, and the wear tests were performed in dry sliding conditions. XRD analyses confirm the formation of δ-TiN and tetragonal ɛ-Ti 2N phases in the modified layer. It was observed that the surface hardness and wear resistance increase as the treatment time and temperature increase. The electrochemical impedance measurements indicate a decrease in double layer capacitance value and increase in charge transfer resistance for the nitrided specimens compared to the untreated ones.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.