Abstract
Abstract Diamond CVD on a cemented carbide (WC–Co) substrate pretreated using an N2–C2H2 plasma has been investigated. The quality of a diamond film deposited on a plasma carbonitrided substrate pretreated at 600°C by N2–C2H5(5%) plasma was much better than that of a substrate pretreated by a conventional process which consisted of chemical etching and scratching with diamond powder This is because Co diffusion into the diamond and the formation of amorphous or graphitic carbon were suppressed by this plasma pretreatment. Moreover, the adhesion of the deposited film to the substrate was improved. From the results of X-ray diffraction, it was estimated that such advantages of this pretreatment originated from the formation of Co2N on the surface of cemented carbide. On the other hand, diamond film was not observed on the substrate pretreated by N2 plasma, and furthermore, decarburization and formation of metallic tungsten occurred from decomposition of part of the WC. Accordingly it can be concluded that plasma carbonitriding is a very effective pretreatment process in order to synthesize a high quality diamond film on a cemented carbide substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.