Abstract
With the aim to obtain a scaffold with improved mechanical properties with respect to collagen for tendon augmentation and regeneration, a novel collagen-based material was prepared via heterogeneous phase derivatization of type I collagen sponges using polylactic acid. Compared to the untreated collagen, the functionalized sponge (Coll-PLA) was characterized by higher tensile properties and lower swelling capability; the degradation rate of Coll-PLA, in the presence of collagenase, was lower than that of the untreated collagen sponge. These results are related to an increased hydrophobic character of the collagen matrix due to the presence of PLA chains. In vitro tests, performed with human primary fibroblasts, showed that cell adhesion and proliferation rate on Coll-PLA were comparable to those obtained with the non-functionalized collagen. These findings suggest that the new biomaterial could be suitable as scaffold in tendon augmentation and regeneration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.