Abstract
Piezoelectric ceramics with excellent piezoelectric properties and a high Curie temperature are important for numerous electromechanical devices in a broad range of temperature environments. In this work, the relaxor ferroelectric Pb(Yb1/2Nb1/2)O3 end member was selected to be introduced into a BiScO3-PbTiO3 high-temperature piezoelectric ceramic to reduce the dielectric loss and improve the piezoelectric properties while slightly reducing the Curie temperature. The phase structure and dielectric, ferroelectric and piezoelectric properties of 0.025Pb(Yb1/2Nb1/2)O3-(0.975−x)BiScO3-xPbTiO3 (0.60 ≤ x ≤ 0.63) ceramics were systematically analyzed, and the best electrical properties were observed in the morphotropic phase boundary region x = 0.61 with d33 = 370 pC/N, kp = 44%, Pr = 33.9 μC/cm2. Importantly, no significant depolarization was observed in the x = 0.61 ceramic from room temperature to 290 °C, demonstrating its good thermal stability and potential applications in a wide range of temperature environments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.