Abstract
Ceramics are highly valued for their exceptional thermal resistance and ability to withstand high temperatures. This study investigated the production of ceramic-like pressed geopolymer, focusing on the effects of aging period and sintering temperature. The results showed that the 7-day pressed geopolymer achieved the highest compressive (134.7 MPa) and flexural (34.9 MPa) strengths after sintering at 1000°C, with a density retention of 93.7 %, a mass loss of 7.9 %, and a thermal shrinkage of 1.4 %. Microstructural analysis at 1000°C showed a dense ceramic-like structure with nepheline formation. Phase analysis of the 7-day pressed geopolymer revealed a decrease in the amorphous phase as temperature increased, with nepheline formed at 800°C (26.0 %) and maximized at 1000°C (61.0 %). This work offers an optimal aging period and sintering temperature to maximize the mechanical strength and nepheline crystal formation, making them perfect for fire-resistant panels and precast construction products.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.