Abstract

Polycrystalline ternary AgIn 5S 8 films were deposited on indium–tin-oxide coated glass substrates by using chemical bath deposition. New procedures for the growth of films are presented. The solutions containing silver nitrate, indium nitrate, triethanolamine, ammonium nitrate, and thioacetamide under acidic conditions were used for the deposition of AgIn 5S 8 polycrystalline films. The influences of various deposition parameters on structural, optical, and electrical properties of films have been investigated. The X-ray diffraction patterns show cubic AgIn 5S 8 is the major crystalline phase. With different substrates, the different crystalline phases were observed. The band gaps and carrier densities of these samples determined from transmittance spectra, electrochemical and Hall measurements are in the range of 1.73–1.85 eV and 4.35 × 10 14 to 6.53 × 10 14 cm −3, respectively. The flat band potentials of these samples are located between −0.31 and −0.41 V versus normal hydrogen electrode by using the Mott–Schottky measurements. All samples indicated n-type conductivities by electrochemical and Hall measurements. The maximum photocurrent density of samples prepared in this study was found to be 4.5 mA cm −2 under the illumination using a 300 Xe lamp system with the light intensity kept at 100 mW cm −2.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.