Abstract
In South Africa, coal represents the primary source of energy used for electricity generation. Coal power plants use the wet flue gas desulfurization (WFGD) process to remove sulfur dioxide (SO2) from their flue gas. However, this technology produces a large amount of synthetic gypsum, resulting in waste disposal and environmental pollution. This study investigated the physical, chemical and geotechnical properties of WFGD gypsum and its potential application to develop cement-free bricks. WFGD gypsum was collected from a coal power plant in South Africa. It was found that the principal oxides of WFGD gypsum were sulfur trioxide (SO3) and calcium oxide (CaO), which represented more than 90% of the total weight. Calcium sulfate (CaSO4) and calcium di aluminate (CA2) were the predominant minerals in the raw material. The density of the WFGD gypsum was 2.43 g/cm3. The maximum dry density and optimum moisture content values were 1425 kg/m3 and 18.5%, respectively. WFGD gypsum had a liquid limit of 51% but did not display any plasticity characteristics. The optimum curing temperature of gypsum bricks was 40 °C. WFGD gypsum-based bricks exhibited compressive strength of up to 2.3 MPa and a density of about 28% less than that of typical clay bricks. Additionally, there was no significant decrease in compressive strength after seven wet/dry cycles. These results show that WFGD gypsum could be used to produce lightweight building materials with low strength requirements.
Highlights
Human population growth and industrialization have led to a need to generate more electric power [1]
The results showed that wet flue gas desulfurization (WFGD) gypsum was found to have a maximum dry density (MDD) of 1425 kg/m3 and optimum moisture content (OMC) of 18.5%
It was found that WFGD gypsum consisted mainly of sulfur and calcium, which had a total weight of more than 90%
Summary
Human population growth and industrialization have led to a need to generate more electric power [1]. An example of a technology developed is wet flue gas desulfurization (WFGD) [5]. Due to its high desulfurization efficiency and low operating costs, the wet limestone system is the most commonly used [6]. This technique produces a large quantity of synthetic gypsum, resulting in a problem with waste disposal and pollution. In 2008, US and European factories produced almost 30 million tons of WFGD gypsum, of which less than 75% was recycled [8]. This problem necessitates plans to beneficiate, reuse and recycle these waste materials
Sign-in/Register to view highlights & summary Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.