Abstract
AbstractBenzoylhydrazide compounds were evaluated as a nucleating agent for poly(L‐lactic acid) (PLA). From the results of the differential scanning calorimetry, octamethylenedicarboxylic dibenzoylhydrazide (OMBH) was found to be most effective for acceleration of PLA crystallization under higher cooling rate of −50°C min−1. PLA with OMBH of 1 wt % exhibited very short crystallization half‐time with wide range of isothermal temperature from 90 to 130°C. The molding cycle time of PLA with OMBH in injection molding was less than 3 min, and the cooling time was one‐third of ethylenebis(12‐hydroxystearylamide)/talc system as a nucleating agent. Physical and mechanical properties improved extremely, and the heat distortion temperature of 124°C, flexural modulus of 4.1 GPa, and Izod impact strength of 7.9 kJ m−2 were achieved. This indicates that the utilization of OMBH makes it possible to extend the application range of PLA as automotive parts and electric appliances, which require higher heat resistance and stiffness. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 244–250, 2007
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.