High-density (with a relative density of up to 98.8%) ultra-high-temperature ceramic materials (UHTCs) based on the ZrB2–TaC–SiC system were obtained by hot pressing for 15 min at 2000°C 30 MPa of pressure in an argon atmosphere. Phase composition, lattice parameters, microstructure, flexural strength, Vickers hardness and crack resistance were studied. The maximum values of strength, hardness and crack resistance were 440 MPa, 20.3 GPa and 5.3 MPa·m1/2, respectively. The effect of the ZrB2/TaC ratio on the lattice constants and the mechanical properties of the material is established.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.