Abstract
Nanocrystalline tin oxide (SnO2) powders have been synthesized by a low temperature chemical precipitation method. As-prepared and heated powders were characterized by XRD, SEM and luminescence studies. Crystallographic parameters such as crystallite size, lattice parameters and dislocation density in SnO2 nanocrystalline powders were calcu- lated by Rietveld analysis. The average crystallite size of 9 - 43 nm was obtained for SnO2 powders through controlled heat treatment process. The washed powders morphology was almost spherical in shape and average agglomerate crystal size was between 0.2 - 0.4 μm. A Photoluminescence (PL) study was measured at an excitation wavelength of 265 nm for as-prepared and annealed powders; it showed a broad emission peak at 417 nm for all powders. The highest PL emission was attained for the powder annealed at 500℃. The synthesized nanocrystalline SnO2 oxide semiconductor material could be suitable for making optoelectronic and sensor devices.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.