Photoluminescence (PL) from alkyl-terminated silicon nanocrystallites as a function of size has been studied. Ultraviolet–blue luminescence (390–410 nm) is observed from as-prepared silicon nanoclusters with diameters from 3 to 8 nm. After 1 h of annealing at 162°C in 2-methoxyethyl ether (diglyme), the λ max of PL shifts from 360 to 420 nm. High-resolution transmission electron microscopy (HRTEM) images show that individual silicon nanoparticles are fused to form pairs of nanoparticles. FTIR spectra show that the alkyl groups remain on the surface of silicon nanoparticles. As the temperature is raised to 250°C for 1 h, the PL no longer shows any peak in the visible light region. TEM images show that the silicon nanoparticles are aggregated and fused uniformly in one single dimension, to form a strip, and these strips parallel each other. When the temperature is raised to 350°C these silicon nanoparticles form a large piece of silicon textile network, showing that functionalized alkyl surface does not persist above this temperature. A strong Si–O–Si asymmetric stretching vibration appears between 1000 and 1100 cm−1 at the expense of the C–H vibrational modes and there is no more change after 3 h of annealing at 250 or 350°C. These results provide strong evidence that the PL originates from quantum confinement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.