Abstract
The luminescence in SrAl 2 O 4 : Eu 2 + , Dy 3 + under continuous excitation is quite different from the “standard” intra-ion photoluminescence (PL) and gradually grows during hundreds of seconds before reaching the saturation (photo-charging effect). In this work, we report the behavior of photo-charging effect under the blue and UV light irradiation at temperatures between 20 and 370 K, as well as afterglow (AG) and thermoluminescence (TL) observed after the irradiation termination. At 20 K the photo-charging effect is absent. With increasing temperature the photo-charging effect appears as a result of PL decreasing due to competitive trapping process with activation energy of 0.17 eV. The AG decay curves are described well by the Becquerel's law with the exponent close to 1. The AG decay time is about 10–50 s and practically does not depend on temperature. The TL glow curve exhibits at least seven partially overlapped peaks with maxima at 50, 65, 80, 155, 200, 250 and 290 K. The emission spectra of Eu 2 + consist of two bands at 450 and 520 nm. Both the bands are the same for the PL, AG and TL spectra, but their ratio depends on temperature and the luminescence type.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.