Abstract
Three series of amorphous copolymers containing azobenzene groups with various substituents and certain amounts of crosslinkable acrylic groups were prepared. The cross-linked polymer films were obtained by thermal polymerization of the acrylic groups in the copolymers, during which, by controlling the time of cross-linking reaction, the films can be made with different cross-linking degree (from 0 to 32%, which was monitored by FT-IR spectra measurement). Photo-induced alignment process of the films was performed under irradiation with linearly polarized light at 442 nm, and the effect of cross-linking degree on the photo-induced alignment rate was investigated. The dynamics of the photo-induced alignment was analyzed with biexponential curve fitting. The photo-induced alignment rate and the maximum transmittance of the films decreased because of the cross-linking. Furthermore, for the cross-linked samples, it was found that their saturated value of transmittances keep constant after repeated writing and erasing cycles. The findings reveal that the cross-linking of the film can effectively restrain the phototactic mass transport of azopolymer during irradiation by polarized light. The relationship between the cross-linking degree and the photo-induced alignment behavior of azopolymer is discussed in detail.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.