Abstract
Barium was deposited at room temperature on a thermal silicon oxide layer and the interfacial reaction was monitored by synchrotron induced photoemission (both core level and valence band). The first step of the growth consists of an interfacial reaction which leads to the formation of an interfacial silicate layer. The next step consists in formation of barium oxide while metallic barium occurs subsequently. The deposit can be also homogenized by annealing above 575 K. This results in the formation of several layers of silicate by consumption of silicon oxide. In the case of fractional coverage, subsequent annealing at 975 K induces the decomposition of barium silicate. However, such a decomposition process is strongly dependent on the initial film thickness. It can be avoided for deposits thicker than 3 eqML.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.