We present the results of the electronic band structure study of the Ge0.9Mn0.1Te epilayers, clean and modified in situ by deposition of manganese atoms under ultra high vacuum conditions. Ge1-xMnxTe is a ferromagnet with a relatively high Curie temperature (up to 140 K) strongly depending on Mn concentration [1]. Thus, investigation of its properties, including the band structure, attracts considerable interest, in view of possible applications of IV-VI-based systems in fabrication of spintronic devices. The Ge0.9Mn0.1Te layers were grown on BaF2 (111) substrates by an MBE method with use of effusion cells as GeTe, Te2 and Mn solid sources. The substrate temperature was 400-450 o C. The content of Mn in Ge0.9Mn0.1Te was checked by energy dispersive X-ray fluorescence analysis. The sample surface was protected by a layer of amorphous tellurium. Prior the photoemission experiments, the tellurium layer was removed by annealing. The Mn overlayers were deposited in situ at room temperature. The valence band and shallow core levels of Ge0.9Mn0.1Te and ultrathin Mn overlayers have been investigated by means of resonant photoemission spectroscopy (RPES). In this technique the radiation energy is tuned to the intra ion transition (like Mn 3p-3d) in order to enhance emission from partly occupied shells of transition metal atoms. Sets of resonant photoemission spectra were measured for the photon energy range covering the energy of the Mn 3p→3d transition (40<hν<60 eV). They were acquired for the clean surface of the Ge0.9Mn0.1Te sample, after evaporation of 0.5 ML Mn and after annealing at 200 o C for 2 hours. The annealing was carried out in order to induce the diffusion of Mn atoms into the Ge0.9Mn0.1Te crystal. The spectra (photoelectron energy distribution curves) covered the range of electron binding energy starting from the valence band edge down to the Mn 3p level. The Mn 3d states contribution occurred in the upper part of the valence band, with a maximum at the binding energy of about 4 eV. Its shape corresponded to that expected for Mn 2+ ions surrounded by six Te ions in the octahedral coordination [2]. Deposition of Mn and annealing the system led to an increase of Mn 3d feature intensity but did not induce any change in the shape of the spectrum. This proved that diffusing Mn ions occupied the same sites in the lattice as those introduced during the layer growth. The results acquired for the Ge0.9Mn0.1Te epilayers are compared with those recently obtained for bulk Ge1-xMnxTe polycrystals in which Mn possibly forms a mixed valence system [3]. The photoemission results are also related to perceptible differences in magnetic properties of theses two systems.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.