Abstract
Acidic sols of TiO2, ZrO2 and Ti-Zr mixed oxide precursors were prepared. The sols were then smeared on quartz substrate and annealed at 650 degrees C for 2 hour to form polycrystalline oxide films. XRD, SEM, UV-visible absorption spectra and XPS were carried out to characterize the films. It was found that the crystalline phase of pure titania is an anatase and pure zirconia is a tetragonal. The binary oxides show the anatase phase at the molar ratio of Ti:Zr = 2.73:1, which means that solid solution was formed. The absorption edge of the TiO2-ZrO2 binary oxides showed obvious blue shift as the Zr ratio increased. The results obtained indicate that the band gap of the binary oxides could be adjusted from 3.2 eV (TiO2) to 7.8 eV (ZrO2) by varying the molar ratio of Ti and Zr. Au interdigitated electrodes were produced by planar technology and MSM (metal-semiconductor-metal) structure UV detector based on TiO2-ZrO2 binary oxides was fabricated. Obvious photoelectric response was observed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.