Abstract
Abstract Phosphorus as an alloy element is quite common in powder metallurgy, the contents industrially used being markedly higher than those present in wrought steels. In this study, the influence of phosphorus addition through different P carriers was investigated. PM steels of the type Fe-0.7%C-x%P (x = 0.0 … 0.8%) were manufactured by pressing and sintering in H2. It showed that Fe3P is the best phosphorus carrier, resulting in fine and regular microstructure and in high impact energy data at 0.3 … 0.45%P while red P and also Fe2P showed a tendency to agglomeration, with resulting secondary porosity. At high P levels the mechanical properties tend to drop, for the tensile strength at P > 0.60%P while for the impact energy the threshold is 0.45%P. The dimensional behaviour of Fe-C-P can be related to PM aluminium alloys, expansion by transient liquid phase being followed by shrinkage by persistent liquid phase, at least at higher temperatures. In contrast to the dimensional behaviour, degassing and reduction is hardly affected by the phosphorus content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.