Abstract
A combination of XRD, solid-state NMR and state-of-the-art imaging techniques were used to investigate how the calcium orthophosphate/calcium silicate ratio affects the crystallisation of bioactive glasses in the system SiO2-P2O5-CaO-CaF2. In the phosphate-free glass, xonotlite, wollastonite and cuspidine crystallised. From 2.4 mol% P2O5, fluorapatite also formed, while the amount of wollastonite decreased. Crystallisation tendency was low for low phosphate contents, while above 3 mol% P2O5 it increased. The phosphate-free glass showed a volume crystallisation mechanism with constant activation energy. By contrast, the glass with the largest phosphate to silicate ratio showed both volume and surface crystallisation, causing a pronounced decrease in activation energy with crystallisation degree. This work shows that by changing the phosphate/silicate ratio we can determine which crystal phases form, obtaining for example fluorapatite-free or wollastonite-free glass-ceramics, depending on the desired application and properties such as mechanical strength or activity in contact with physiological solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.