Abstract
The dual role of electric field in the flash sintering process of conducting MnCo2O4 is demonstrated. The flash and conventionally sintered MnCo2O4 samples produced at different temperatures are characterized using energy dispersive X-ray and micro-Raman spectroscopy to elucidate the micro-level spatial distribution of evolved phases. Raman signal mapping over the two ways sintered samples exposes differently grown areas of cobalt oxide based secondary phase. Electrical conductivity of conventionally sintered sample is recorded as a function of temperature and E-field and is utilized to discover the charge carrier activation mechanism during the flash effect. The conductivity before the flash-onset is shown to be comparable to that occurs by Poole-Frenkel effect and Phonon-assisted tunneling i.e. by the mechanism that occurs before the dielectric breakdown of semiconductors and insulators. The observed results, finally, confirm that catalyst like drift action of E-field on cobalt oxide formation is responsible for enhancement in the flash-sintering.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.