Abstract
Lead-free (Ba0.85Ca0.15)(ZrxTi1−x)O3 (BCZT,0.03≤x≤0.25) ceramics were synthesized in a wide compositional range to investigate the relationship between its phase diagram and electromechanical properties. The effects of Zr content on microstructure, phase transition behavior, ferroelectric, dielectric, piezoelectric and strain properties of BCZT ceramics were systemically studied. The morphotropic phase boundary (MPB) of BCZT ceramics was closely connected with the presence of orthorhombic phase between rhombohedral and tetragonal phases at a narrow region, which could meet in a region that is termed the diffuse ferroelectric phase transition region (DPTR) in this work. As a result, the composition x=0.08 located at near MPB region close to tetragonal phase side exhibited the outstanding electrical behavior at room temperature: d33=349pC/N, kp=43%, S=0.185% and Smax/Emax=463pm/V. Furthermore, pure electrostrictive effect with large electrostrictive coefficient Q11 of 0.036m4C−2 had also been observed in the composition x=0.20, and large Q11 of MPB composition showed superior temperature stability in the investigated temperature range.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.