Abstract
Nanostructured disordered iron–aluminium–copper alloy of Fe–30% Al–20% Cu composition was prepared by mechanical alloying of the elemental powders in a high-energy ball mill. The transformations occurring in the material during milling were studied with the use of X-ray diffraction. The transformation of the phase depends upon the milling time. With the increase of milling time all Al and Cu atoms became dissolved in the bcc Fe and the final product of the MA process was the nanocrystalline Fe(Al,Cu) solid solution with a mean crystallite size of about 9 nm. Scanning electron microscopy (SEM) was employed to examine the morphology of the samples as a function of milling times. Magnetic properties were also investigated and were related to the microstructural changes. The unprocessed sample showed a soft ferromagnetic behavior (Hc ≈ 173 A/m) whereas alloyed samples at the early stages of processing reached a hardening ferromagnetic behavior (Hc ≈ 15277 A/m). For longer milling time the magnetic behavior slightly softened becoming a semihard ferromagnetic (Hc ≈ 5500 A/m).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.