Abstract
Amorphous/nanocrystalline 50 Ni –50 Ti powders were synthesized from elemental Ti and Ni powders by solid state synthesis utilizing low energy mechanical alloying with times up to 100 h. The produced powders were investigated by X-ray diffraction and differential scanning calorimetry to study phase transformations that occurred during heating in the calorimeter. It was found that at the first stage of the heating process, a disordered NiTi phase was formed at temperature of about 400°C. Further investigations indicated that this phase transformed into the Ni 3 Ti and Ti 2 Ni intermetallic compounds after heating at a temperature of about 800°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.