Phase Transformations and Microstructural Observations During Subcritical Heat Treatments of a High-Chromium Cast Iron

Abstract

In this study, Cr white iron of 18.23 wt.% was subjected to a series of subcritical heat treatments. At both temperatures of 350 and 450 °C, no precipitation of secondary carbides was observed, and the overall microstructure resembles to that of the as-cast condition. At 550 °C, hardness values increased slightly compared to the as-cast values. No evidence of secondary carbide formation was observed. At 650 and 750 °C, extensive-to-complete transformation to pearlite-ferrite structures has occurred. Some evidence of secondary carbide precipitation especially for prolonged treatment periods was not adequate to obstruct the hardness decrease due to the dominating effect of pearlitic-ferritic formation. At 850 °C, secondary carbide precipitation and martensite formation lead to high hardness values.