Abstract
We report on experimental investigations of a Ni2.36Mn0.64Ga Heusler alloy, which transforms to tetragonal martensite at cooling below Ms ≈ 271°С. The evolution of lattice constants was tracked by in situ neutron diffraction measurements. It was found that the martensite tetragonality c/a gradually decreases during heating from room temperature to austenite transition start temperature As ≈ 272°С. The phenomenon of martensite stabilization was investigated by differential scanning calorimetry utilizing three different protocols of the martensite aging. It was found that the martensite aging at a constant temperature T = 255°С merely shifts the reverse transformation to higher temperatures, while the reverse transformation temperature interval (Af – As) remains the same (≈ 30°C) independently of aging time. On the other hand, a multistep aging at different temperatures starting from T = 255°С not only shifts the reverse transformation temperature, but makes the transformation temperature interval narrower down to As – Af ≈ 10°C.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call