Abstract
Sn-filled and Fe-doped CoSb3 skutterudites were synthesized by encapsulated induction melting. A single δ-phase was obtained by subsequent annealing, as confirmed by X-ray diffraction. The as-solidified ingot consisted of mixed phases of -CoSb, -CoSb2, δ-CoSb3 and elemental Sb. The phases could be transformed by annealing, and the phases of the as-solidified ingot annealed at 773 K for 24 h transformed to δ-CoSb3. The temperature dependence of the Seebeck coefficient, electrical resistivity and thermal conductivity were examined from 300 K to 700 K. The positive Seebeck coefficient confirmed p-type conduction. The electrical resistivity increased with increasing temperature, which showed that the SnzCo3FeSb12 skutterudite is highly degenerate. The thermal conductivity was reduced by Sn-filling because the filler atoms acted as phonon scattering centers in the skutterudite lattice. The thermoelectric figure of merit was enhanced by Sn filling and its optimum composition was considered to be Sn0.3Co3FeSb12.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.