Abstract
Fe-18Cr-8Ni and Fe-18Cr-8Ni-1Y (at%) stainless steel powders were nanostructured by mechanical alloying from elemental powders and subjected to 90min annealing treatments at various temperatures. The microstructural evolutions as a function of alloy compositions and temperatures were investigated by in-situ and ex-situ x-ray diffraction experiments, transmission electron microscopy and focused ion beam microscopy. The dependence of hardness on the microstructure was utilized to study the mechanical changes. It was found that the resulting microstructures by mechanical alloying were bcc solid solution, the so-called α’-martensite structure. The high temperature in-situ x-ray diffraction experiments showed that the martensite-to-austenite reverse phase transformation was completed above 800 and 900°C for Fe-18Cr-8Ni and Fe-18Cr-8Ni-1Y steels, respectively. A partial or complete retransformation to martensite was observed upon cooling to room temperature. Annealing of nanocrystalline Fe-18Cr-8Ni steel yielded grain growth reaching to micron sizes at 1100°C while addition of 1at% yttrium stabilized the microstructure around 160nm grain size and 6GPa hardness after 90min annealing at 1200°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.