Abstract
The KxNa(1-x)NbO3 (x = 0.45, 0.46, 0.47, 0.48, 0.49, 0.50) lead-free piezoelectric ceramics was fabricated by conventional solid-state sintering method. It was found that the ratio of alkaline metal would affect the microstructure, bulk density, and optimum sintering temperatures of ceramics. Meanwhile, the electrical properties were also influenced by modulating the K/Na ratio, exhibiting corresponding composition-dependent properties. The optimum electrical properties of KxNa(1-x)NbO3 such as piezoelectric constant d33 = 115 pC/N, mechanical quality factor Qm = 20, Curie temperature Tc = 365 °C, eT33/e0= 588.1, dielectric loss tan δ = 0.024, bulk density (ρ) = 3.08 g/cm3, remnant polarization (Pr) = 8.87 μC/cm2 and coercive field (Ec) = 13.79 kV/cm were obtained at x = 0.46.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.