Abstract
NbSi2- and TaSi2-based electroconductive ceramic composites with the addition of 40–70 vol% Al2O3 and ZrO2 particles were fabricated by high-temperature sintering (1400–1600 °C) under argon. Their phase stability, microstructural evolution, oxidation kinetics and electrical properties were studied at high temperatures. The densification of the composites was improved by increasing the oxide phase content and sintering temperature. The interaction of the starting metal disilicides with residual oxygen sources resulted in the formation of the hexagonal-structured 5–3 metal silicide (Nb5Si3 and Ta5Si3) phases. The increasing sintering temperature and volume percentage of the oxide phase reduced the pest oxidation, particularly for the silicide–alumina composites, which exhibited lower oxidation-induced mass changes than their dense monolithic metal silicides. Depending on the silicide–oxide volume percentage, their electrical conductivities ranged from 5.3 to 111.3 S/cm at 900 °C. Their phase stability, reduced oxidation rates and high electrical conductivities at high temperatures show promise for future high-temperature applications in advanced sensing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.