Phase stability and transport characteristics of (ZrO2)1-x(Sc2O3)x(СeO2)y and (ZrO2)1-x-y-z(Sc2O3)x(СeO2)y(Y2O3)z solid solution crystals

Abstract

Phase stability and transport characteristics of (ZrO2)1-x(Sc2O3)x(СeO2)y (x = 0.08–0.10; y = 0.005–0.015) and (ZrO2)1-x-y-z(Sc2O3)x(СeO2)y(Y2O3)z (x = 0.08–0.10; y = 0.005–0.010; z = 0.005–0.020) melt-grown crystals have been studied after air heat treatment at 1000 °C for 400 h.Annealing of the (ZrO2)1-x(Sc2O3)x(СeO2)y crystals caused the formation of a rhombohedral phase and reduced the electrical conductivity of the specimens in the entire test temperature range. Yttrium co-doping of the (ZrO2)1-x(Sc2O3)x(СeO2)y crystals stabilized the cubic phase for some compositions. In two-phase (ZrO2)1-x-y-z(Sc2O3)x(СeO2)y(Y2O3)z crystals containing a cubic and a tetragonal phases exhibited conductivity degradation. Annealing of cubic crystals caused the formation of the t'` phase and increased their conductivity.