Abstract
AbstractThe final morphology of cured blends based on unsaturated polyester, styrene, and low‐molar‐weight saturated polyester as a low profile additive (LPA) was investigated with atomic force microscopy and scanning electron microscopy. The observed structure was compared to those obtained with widely used poly(vinyl acetate) (PVAc). On the surface and in the bulk, a network of particles, ranging in size from 50 to 60 nm, was observed with saturated polyester as an LPA. The influence of the molar weight and LPA content was investigated. To determine the mechanism of formation of such a morphology, in situ experiments were carried out to elucidate the phase‐separation mechanism. Small‐angle laser light scattering and small‐angle neutron scattering experiments were performed on ternary blends containing PVAc and saturated polyester, respectively. The first stage of spinodal decomposition was observed in both cases. Within our experimental conditions, gelation froze further evolution and led to a two‐phase cocontinuous structure that imposed the final morphology characteristics. In particular, the period and amplitude of the concentration fluctuations generated during the phase separation played essential roles. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 95: 1459–1472, 2005
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.