Abstract
Al–TM–RE (TM: transition metal, RE: rare earth metal) and Al–RE alloys were analysed with the aim of studying phase selection under various processing conditions. The metastable phases formed in binary Al-rich systems (notably Al–Sm) are revised for a unified interpretation of the literature. Two groups of alloys had different behaviour as for phase selection. In Al 88Fe 9Nd 3 and Al 87Ni 10Ce 3 stable intermetallic compounds form as primary phases during solidification. Nanocrystalline Al is formed at high undercooling. This may occur directly in rapid solidification or when fully amorphous materials are suitably annealed. In Al 90Sm 8Ni 2 and Al 90Sm 8Fe 2 metastable intermetallics form during rapid solidification together with a fraction of amorphous phase, whereas nanocrystalline Al forms on annealing the amorphous phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.