Abstract
The phase relation in the β phase AuxCu55-xZn45 ternary alloys was studied. There appear two types of ordered phases, i.e., the Heusler-type and the CsCl-type superlattices, and a martensite structure at low temperatures. The critical temperature (Tc) of CsCl-type superlattice becomes higher than that (455°C) of the Cu-Zn binary alloy with the increase in Au content. Tc of the Heusler-type has a maximum (390°C) near the stoichiometric composition of AuCuZn2. The martensitic transformation temperature (T0) increases up to a maximum (45°C) at the 26 at.% Au and then decreases with the further increase in Au content. The nature of the stability of the β phase was discussed from the view point of ionic radii of the constituent elements, electron atom ratio and quenched-in vacancies.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.