Abstract
Yttrium aluminum garnet (YAG) powders were synthesized by precipitation of hydroxides using three types of precursors: nitrates (nitrate process), isopropoxides (alkoxide process), and isopropoxides chelated with ethyl acetoacetate (modified alkoxide process). The phase development in the powders during heat treatments was investigated with DTA and XRD. An intermediate hexagonal YAlO3 (YAH) phase was formed at 800°C in all powders regardless of the synthesis processes, but its complete transformation to YAG at higher temperatures (≥1000°C) occurred only in the powders prepared by the nitrate and modified alkoxide processes. The alkoxide process led to the largest deviation from the bulk composition, producing a single phase of YAH that transformed into YAG plus a stable YAM (Y4Al2O9) phase. The modified alkoxide process led to the most homogeneous bulk composition, resulting in the least amount of YAH in the powder. The poor chemical homogeneity in the powders prepared by the nitrate and alkoxide processes was attributed to the segregation of the hydroxides and to the presence of the double alkoxide, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.