Abstract
ZnO doped with Bi 2O 3 and Sb 2O 3 (ZBS), is the basic system for ceramic varistors. Phase formation during sintering of ZBS was measured in situ, using 1 mm thick samples and synchrotron X-rays. Sintering shrinkage was measured in different atmospheres by an optical method. Thermodynamic calculations were performed to explain phase formation, composition, stability of additive oxides and influence of the oxygen fugacity on sintering. Sb 2O 4, pyrochlore, trirutile and spinel were formed at temperatures of 500–800 °C. The oxidation of antimony was controlled by the oxygen partial pressure and affected both, phase formation and sintering kinetics, in the ZBS system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.