Abstract
The compositional regions for primitive (P) and face-centered (F) icosahedral quasicrystals (iQc) have been determined to be around Zn 84Mg 9Zr 7 and Zn 75Mg 18Zr 6, respectively. A 1/1 approximant of the F-type iQc was found to have a composition around Zn 77Mg 18Zr 5. A similar tendency has been verified for the Zn–Mg–Hf system. No stable iQc was observed in the Zn–Mg–Ti system. High-resolution X-ray measurements performed with synchrotron radiation showed that the stable iQcs are highly ordered and contain less phason disorder. High-angle annular dark field (HAADF) scanning transmission electron microscopy observation of the 1/1 Zn–Mg–Hf approximant effectively revealed the Hf positions in the structure, whose local contrasts can be reasonably interpreted by a structural model where icosahedral and dodecahedral Hf clusters are mutually interpenetrated. Similar appearances of local contrasts were frequently observed in HAADF images of the F-type iQc, indicating that the iQc structure is also build up of icosahedral clusters that are almost identical to those in the 1/1 approximant.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.