Abstract
This paper investigates the processes of phase formation of solid solutions of (1 − x)BaTi0.85Zr0.15O3 − xAgNbO3 where x = 0, 0.03, 0.06, 0.09. The optimal temperatures of synthesis and sintering are determined. From the results of X-ray diffraction analysis, it follows that all solid solutions have a perovskite-type structure. Analysis of the microstructure showed that the average grain size decreases at concentrations x = 0.03 and 0.06. Correlations between the cationic composition and dielectric characteristics of the studied solid solutions have been established. The values of the total stored energy and efficiency are determined. The maximum stored energy was found for a solid solution with x = 0.03 and amounted to 0.074 J∙cm−3 with an efficiency of 76.5%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.