Phase evolution, Raman spectroscopy and microwave dielectric behavior of (Li1/4Nb3/4) doped ZrO2-TiO2 system

Abstract

The phase evolution, Raman spectroscopy and microwave dielectric properties of (Li1/4Nb3/4) doped ZrO2- TiO2 system were investigated. The effects of the Zr/Ti ra- tio and the (Li1/4Nb3/4) substitution were addressed. X-ray diffraction and electron diffraction analysis showed that the crystalline phases of the (Li1/4Nb3/4) doped ZrO2-TiO2 ce- ramics depended greatly on the Zr/Ti ratio. The sample with Zr/Ti ratio of 7/9 crystallized as Zr5Ti7O24 phase structure, a commensurate structure with a tripled a-axis superstruc- ture and aZ TT ZTT sequence. Secondary phase of mono- clinic ZrO2 phase appeared when the Zr/Ti ratio was as high as 9/7. Raman analysis showed that the Raman peaks located at 651 and 624 cm −1 were assigned to the vibration modes of Zr-O octahedron and Ti-O octahedron, respec- tively. The dielectric constant and quality factor (Qf value) of the (Li1/4Nb3/4) doped ZrO2-TiO2 ceramics decreased slightly as the Zr/Ti ratio changed from 6/10 to 9/7. The temperature coefficient of resonate frequency (TCF value) was sensitive to the Zr/Ti ratio and it showed a negative value when the Zr/Ti ratio was close to 5:7. Meanwhile, the TCF value of ZrO2-TiO2 ceramics could also be tailored by the (Li1/4Nb3/4) substitution.