Abstract
A series of oxides La2 - x Ca x Zr2O7–α (x = 0.00, 0.05, 0.10, 0.15, 0.20) is synthesized. It is found that in samples with the calcium content x = 0.15, 0.20, the second phase Ca0.9La0.2Zr0.9O3 is present in the fraction increasing with the increase in x. The solubility limit of calcium to form solid solutions based on La2Zr2O7 corresponds to x = 0.1. By high-temperature gravimetry, the proton concentration in La1.95Са0.05Zr2O7–α is obtained as a function of temperature in the interval of 300–950°С in Н2О–О2 atmosphere. According to temperature programmed desorption studies, in the temperature range of 400–900°С at least two types of OH defects with different binding energies are present in the oxide lattice. The temperature dependences of conductivity are obtained for La1.95Са0.05Zr2O7–α in dry and humid air atmosphere in the temperature range of 350–800°С by the method of impedance spectroscopy. The electrolyte conductivity in humid air is shown to substantially exceed the corresponding values in dry air, which can be associated with manifestation of protonic conductivity in humid atmosphere. The dependences of oxide conductivity on the oxygen content in the gas phase are determined. The conductivity is divided into its ionic and hole components.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.