Abstract
The Bi-Cu-Ni system is a very significant, because its alloys belong to the group of potential Cu-Ni-based advanced lead-free solder materials for high temperature application. The results of phase equilibria investigation and characterization of the alloys selected in the Bi-Cu0.5Ni0.5 section from bismuth corner with molar ratio Cu:Ni = 1:1, are presented in this paper. The investigations were performed using different experimental methods - DTA, DSC, SEM-EDS, hardness and electrical conductivity measurements, while thermodynamic calculation was done according to the CALPHAD method using PANDAT software.
Highlights
Može se primetiti da sa porastom sadržaja bizmuta u leguri vrednost tvrdoće opada
The investigations were performed using different experimental methods – diferencijalne termijske analize (DTA), DSC, SEM-EDS, hardness and electrical conductivity measurements, while thermodynamic calculation was done according to the CALPHAD method using PANDAT software
Summary
Ispitani uzorci su odabrani duž vertikalnog preseka Bi-Cu0.5Ni0.5 u sistemu Bi-Cu-Ni. Uzorci su pripremljeni indukcionim topljenjem čistih metala u zaštitnoj atmosferi argona. DTA/DSC ispitivanja su izvođena na uređaju za simultanu termijsku analizu materijala (TGA, DTA, DSC) SDT Q600 (TA Instruments), koji radi u opsegu temperatura od sobne do 1500°C, sa vakuumom do max 7 Pa i brzinom zagrevanja od 0.1 do 100°C/min. Uzorci mase 50 mg ispitivani su uz konstantnu brzinu zagrevanja od 5oC/min. U cilju dobijanja reproduktivnih rezultata svako merenje je ponovljeno, ali nisu pronađena značajna odstupanja temperatura između prve i ponovljene serije DTA/DSC merenja. Električna provodljivost ispitivanih legura merena je pomoću standardnog aparata - SIGMATEST 2.069-Foerster, instrumenta za merenje električne provodljivosti metala i legura, koji ne poseduju feromagnetna svojstva. Ovaj instrument se koristi za merenje električne provodljivosti na osnovu kompleksne impedanse merne sonde. Uzorci su pripremljeni bez upotrebe sredstva za nagrizanje za razvoj mikrostrukture
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call